Andrew Minor, of the Materials Sciences Division in the Department of Energy's Lawrence Berkeley National Laboratory, with colleagues from Hysitron Incorporated and the General Motors Research and Development Center, used the In Situ Microscope at the National Center for Electron Microscopy (NCEM) to record what happens when pillars of nickel with diameters between 150 and 400 nanometers (billionths of a meter) are compressed under a flat punch made of diamond. The transmission electron microscope is equipped so that samples can be stressed, measured, and videotaped while being observed under the electron beam.
"What controls the deformation of a metal object is the way that defects, called dislocations, move along planes in its crystal structure," Minor says. "The result of dislocation slip is plastic deformation. For example, bending a paper clip causes its trillions of dislocations per square centimeter to tangle up and multiply as they run into one another and slide along numerous slip planes."
In general, mechanical deformation tends to increase the number of dislocations in a material. But for small-scale structures, with a much greater proportion of surface area to volume, the process can be very different. The videotaped images from the electron microscope helped the researchers understand why nanoscale nickel pillars are so strong by allowing them to observe changes in the microstructure of the pillars during deformation -- including a never-before-seen process the researchers dubbed "mechanical annealing." (In bulk materials, annealing, a treatment that reduces the density of defects, is usually accomplished by heating.)
Minor says, "The first thing we observed was that, before the test, the nanoscale pillars of nickel were full of dislocations. But as we compressed the pillar, all the dislocations were driven out of the material -- literally reducing the dislocation density by 15 orders of magnitude and producing a perfect crystal. We called this effect mechanical annealing."
The pillars Minor and his colleagues tested were machined from pure nickel using a focused ion beam (FIB), a new technique for small-scale mechanical-compression testing first described in 2004 by Michael Uchic of the U.S. Air Force Research Laboratory and his colleagues. The FIB technique makes it possible to create much smaller structures than the metal "whiskers" first studied in the 1950s, which are made by growing crystals.
Some of the dislocations the researchers observed in the machined pillars were relatively shallow and caused by the ion beams themselves. Others extended through the crystal and were presumably pre-existing defects. Under compression, mechanical annealing caused both kinds of defect to vanish.
"Essentially all the dislocations escape from the crystal at the surface, and you do not get storage of dislocations like you would in larger crystals," Minor says. "What results is a process called 'dislocation starvation,' recently proposed by William D. Nix of Stanford, among others, which has quickly became one of the leading theories of why smaller structures are stronger."
Minor explains, "The idea is that if dislocations escape the material before they can interact and multiply, there are not enough active dislocations to enable the imposed deformation. The structure can only deform after new dislocations are created." This is precisely the process he and his colleagues observed with NCEM's In Situ Microscope, strong evidence that "dislocation starvation" is the correct explanation for the increased strength of small structures.
What happens if a defect-free nanoscale nickel pillar continues to be compressed" Something has to give, which happens when new sources of dislocation "nucleate" in the material. As the existing dislocations disappear in the pillar because of mechanical annealing, the nucleation of new dislocation sources happens at progressively higher stresses.
In the pillar structures, plastic deformation may take the form of sudden flattening, bulging, twisting, or shearing of the pillar, as bursts of new dislocations propagate through it. Or the hardened pillars, made stronger by mechanical annealing, may punch right down into the substrate -- even though pillar and substrate are the same continuous piece of metal. Both processes were captured in the In Situ Microscope's dramatic videotaped experiments.
The FIB machining used by the NCEM researchers produced nickel pillars that were slightly tapered, and the researchers noted that this geometry affected where and how plastic deformation occurred, generally being greater in the smaller-diameter, free end (top) of the pillar.
In larger pillars, those approaching 300 nanometers in diameter, mechanical annealing was not complete, and some dislocations remained visible even after compression. Yet even these pillars exhibited enhanced strength, and progressively higher stresses were needed to continue deformation -- underlining the point that it is the creation of mobile defects that determines strength in these small volumes.
"The beauty of the pillar-testing geometry is that we can straightforwardly define stress. Then we can correlate the measured stresses with discrete plastic events recorded in situ and more clearly interpret the quantitative data from our experiments," says Minor. "The debate over what determines the strength of a small structure has come down to almost a chicken-and-egg question -- is something strong because you need a high stress to move a dislocation that is already there" Or is it strong because you need a high stress to nucleate a new dislocation" In this case, it seems that source nucleation -- that is, the 'egg' -- is the determining factor."
"Mechanical annealing and source-limited deformation in submicrometre-diameter Ni crystals," by Z.W. Shan, Raj Mishra, S.A. Syed Asif, Oden L. Warren, and Andrew M. Minor, appears in the January, 2008 issue of
Nature Materials, advance online publication 23 December, 2007 at
http://www.nature.com/nmat/journal/vaop/ncurrent/full/nmat2085.html .
Source: Lawrence Berkeley National Laboratory
Related stories:
Spiraling nanotrees offer new twist on growth of nanowires
Since scientists first learned to make nanowires, the nano-sized wires just a few millionths of a centimeter thick have taken many forms, including nanobelts, nanocoils and nanoflowers.
Atoms under the mantle
French CNRS scientists have succeeded in modelling the defects of the earth’s mantle responsible for its deformation. These results, obtained using a novel approach which combines numerical calculus and quantum mechanics, constitute the first step towards modelling deformation of this layer and its effects on the mantle. They are published in the March 1st, 2007 issue of
Nature.
Model simulates atomic processes in nanomaterials
Researchers from MIT, Georgia Institute of Technology and Ohio State University have developed a new computer modeling approach to study how materials behave under stress at the atomic level, offering insights that could help engineers design materials with an ideal balance between strength and resistance to failure.
Leibniz Prize winners 2007 announced
The Deutsche Forschungsgemeinschaft (German Research Foundation, DFG) has announced the winners of its 2007 Gottfried Wilhelm Leibniz Prize. At its meeting on 7 December 2006, the DFG Joint Committee named ten scientists and academics — eight men and two women — as recipients of Germany’s most highly endowed research award. For the first time, the prize winners for 2007 will receive up to 2.5 million euros (previously: 1.55 million euros) and be able to use these funds flexibly over a period of seven years (previously: five years) to finance their research.
Metal deformation studies lead to new understanding of materials at extreme conditions
Researchers have found a new tool to explore materials at extreme conditions. By combining very large-scale molecular dynamics simulations with time-resolved data from laser experiments of shock wave propagation through specific metals, scientists at the Lawrence Livermore National Laboratory are now able to better understand the evolution of high-strain-rate plasticity.
A new window into the deformation of nanoscale materials
Materials on the nanoscale don't always have the same properties they would in bulk; for one thing, nanomaterials are often a lot harder. Unlike most bulk materials, a crystal that is small enough can be perfect, free of defects, capable of achieving strength near its ideal theoretical limit.
Researchers find metal gets stronger with three or more line defects
Lawrence Livermore National Laboratory researchers have discovered that three is the magic number when it comes to strengthening metals.
Breakthrough in Nanoscale Understanding of Metal Shape Change
A
nanocrystalline metal is one whose average grain size is measured in billionths of a meter, much smaller than in most ordinary metals. As the grain size of a metal shrinks, it can become many times stronger, but it also usually loses ductility. To take advantage of increasing strength with decreasing grain size, researchers must first understand a fundamental problem:
by what processes do nanosized crystals of metal stretch, bend, or otherwise deform under strain?