SEMATECH and NIST Collaborate on Chemical Analysis of Advanced Gate Dielectrics

Nitrogen incorporation in thin HfO₂/SiO₂ film systems representative of high-k gate dielectric layers in advanced metal-oxide semiconductor field-effect transistors (MOSFETs) has been investigated by synchrotron x-ray photoelectron spectroscopy to elucidate variations in chemical composition between samples annealed in NH₃ and N₂ ambient as a function of temperature. In addition, depth profiling of core-level binding energy spectra has been obtained by variable kinetic energy x-ray photoelectron spectroscopy (VKE-XPS) with tunable photon energy. An HfO₂/SiO₂ “interface effect” has been detected in the Si 1s spectra characterized by a shift of the Si₄+ feature to lower binding energy with no corresponding chemical state change observed in the Hf 4f spectra acquired over a broad range of electron take-off angles.

One of the semiconductor industry’s “grand challenges” is to develop an alternative to the SiO2 gate dielectric that has enabled scaling (increasing integrated circuit device density, according to Moore’s Law) of metal-oxide semiconductor field-effect transistors (MOSFETs) for the past 40 years. The challenge originates from the quest for integrated circuits exhibiting higher speed and lower power consumption, no longer attainable with ultra-thin (sub 2 nm) SiO₂ gate dielectrics due to their high direct tunneling leakage currents. This initiative has given rise to extensive evaluation of Hf-based oxide thin films as promising high permittivity (high-k) replacement material that provides a physically thicker film with lower leakage current characteristics for equivalent SiO₂ capacitance. However, intrinsic properties of hafnia, HfO₂, do not satisfy all requirements for gate dielectrics, particularly, crystallization temperature, defect density, and ion diffusivity. Modification of the hafnia structure has been undertaken by various alloying efforts including nitrogen incorporation to enhance electrical performance.

Thin (3 nm) HfO₂ blanket films deposited by atomic layer deposition on either SiO2- or NH3-treated Si (100) substrates have been subjected to NH₃ and N₂ anneal processing. High-resolution NIST measurements of synchrotron x-ray photoelectron spectroscopy (XPS) were coupled with grazing incidence x-ray diffraction (GIXRD) and electron energy loss spectroscopy (EELS) measurements to elucidate differences in chemical composition and crystalline structure resulting from anneal processing in NH₃ and N₂ ambient as a function of temperature to identify physical evidence for process-dependent transistor performance. Variable kinetic energy XPS (VKE-XPS), achieved via the tunable photon energy capability of synchrotron radiation, was utilized to obtain bulk thin film and interface depth profiling of the core-level electron binding energy spectra.

An “interface effect” characterized by a shift of the Si₄+ feature to lower binding energy at the HfO₂/SiO₂ interface has been detected in the Si 1s spectra illustrated in Figure 1. However, no corresponding chemical state change was observed in the Hf 4f spin-orbit energy spectra acquired over a broad range of electron take-off angles and surface sensitivities, thereby ruling out the likelihood of Hf silicate formation at the interface. The hafnia film has been shown to getter oxygen from the underlying SiO₂, thereby rendering it substoichiometric (oxygen deficient) in the neighborhood of the interface with HfO₂.

The NH₃ anneal ambient has been shown to produce a metastable Hf-N bond component in the Hf 4f XPS spectra corresponding to temperature-driven dissociation kinetics while the Si 2p spectra indicate Si-N bond formation near the HfO2 layer in samples exposed to 700°C/60s/NH3 anneal. GIXRD measurements identify corresponding structural changes resulting from NH₂ (isoelectronic with O) exchange for oxygen in these HfO2 films, although not detected in samples exposed to anneal processing in N₂ ambient. These findings are consistent with elemental profiles across the HfO₂/ SiO₂ /Si(100) interface determined by EELS measurements.

These SEMATECH-NIST results represent a major step toward the controlled optimization of Hf-based gate dielectrics and the development of next-generation MOSFET devices.

Source: Brookhaven National Laboratory

Related stories:

'Phononic Computer' Could Process Information with Heat
Most computers today use electrons to carry information, while theoretical optical computers use photons. Recently, physicists from Singapore have proposed a third type of computer: a “phononic computer,” which would use heat, carried by phonons, to perform operations similar to its electronic counterpart.
XMM-Newton discovers part of missing matter in the universe
ESA’s orbiting X-ray observatory XMM-Newton has been used by a team of international astronomers to uncover part of the missing matter in the universe.
Intel Introduces New Atom Processors for Mobile Internet Devices
Intel Corporation today introduced five new Intel Atom processors and Intel Centrino Atom processor technology for Mobile Internet Devices (MIDs) and embedded computing solutions.
New Intel Server Processors: Fewer Watts, High Performance
Intel Corporation has further increased its energy-efficient performance lead today with the introduction of two low-voltage 45 nanometer processors for servers and workstations that run at 50 watts, or just 12.5 watts per core and frequencies as high as 2.50 GigaHertz (GHz).
Action replay of powerful stellar explosion
Astronomers have made the best ever determination of the power of a supernova explosion that was visible from Earth long ago. By observing the remnant of a supernova and a light echo from the initial outburst, they have established the validity of a powerful new method for studying supernovas.
Researchers visualize complex pigment mixtures in living cells
In a technical advance that could allow researchers to watch cells as they act during the process of photosynthesis, scientists have developed a method that extends the power of fluorescence-mediated bio-imaging to see discrete pigments inside live cells of bacteria.
Intel Ships New Processors Based on 45-nanometer Process
Intel Corporation today announced expanded offerings for embedded market segments with new processors with extended, 7-year life cycle support, a new chipset and a carrier-grade server. The processors, based on Intel's high-k, metal gate transistor formula and manufactured on the company's 45-nanometer process, include the Quad-Core Intel Xeon processor 5400 Series and Dual-Core Intel Xeon processor 5200 Series.
New Light on Dark Energy
Astronomers have used ESO’s Very Large Telescope to measure the distribution and motions of thousands of galaxies in the distant Universe. This opens fascinating perspectives to better understand what drives the acceleration of the cosmic expansion and sheds new light on the mysterious dark energy that is thought to permeate the Universe.

News discussion:

Technology news